Classification: ~T Fe14 (EN 14700)
Open-arc flux cored wire which is developed for hardfacing of wear plates and parts, subjected to high abrasion and low impact.
Price and availability are provided by quotation. Send an enquiry with quantity and variant.
Product description
Open-arc flux cored wire which is developed for hardfacing of wear plates and parts, subjected to high abrasion and low impact. Weld metal has high hardness due to it's high chromium carbide content and machinable only by grinding. Transverse cracks, caused by high hardness level, do not have any negative effect on the abrasion resistance. Typical Applications: Suitable for hardfacing of wear plates, cement conveyor screws, bucket edge and teeth, crusher parts of heavy costruction equipments, catalytic pipes.
Standards and classifications
| EN 14700 | ~T Fe14 |
| TS EN 14700 | ~T Fe14 |
| DIN 8555 | MF 10-GF-65-GR |
Typical chemical values of weld metal
| Type of Analysis | C | Si | Mn | Cr | B | Fe |
|---|---|---|---|---|---|---|
| Weld Deposit | 5.30 | 0.80 | 0.25 | 27.5 | 0,50 | 65.65 |
Typical mechanical values of weld metal
| Test Condition | Hardness (HRc) | Wear Index |
|---|---|---|
| As welded | 62 | 9.8 |
Welding positions
Polarity
Welding parameters and efficiency
| Diameter (mm) | Deposition Rate(kg/h) | Efficiency(%) |
|---|---|---|
| 1.60 | 3.48 | 97 |
| 2.80 | 3.96 | 85 |
Wear resistance
| Property | Level |
|---|---|
| Abrasion | Very High |
| Adhesion | Low |
| Impact | Medium |
| Temperature | High |
| Corrosion | High |
Scale as published in the official Magmaweld chart: Low · Medium · High · Very High
Variants and packaging
| Product Code | Diameter (mm) | Weight Of The Box (kg) | Boxes Per Package | Weight Of The Package | Packaging Type |
|---|---|---|---|---|---|
| 38212GJAM2 | 1.60 | 15.0 | 1 | 15.7 | Wire Basket Spool (K300MS) |
| 38212J2HM2 | 2.80 | 250.0 | 1 | 265.0 | Drum |
Storage and re-drying
- Shouldn t be exposed to high statical load and impact.