Classification: S A MS/CS 1 (EN ISO 14174)
Agglomerated, manganese-silicate type flux for welding general structural steels and pipe steels.
Price and availability are provided by quotation. Send an enquiry with quantity and variant.
Product description
Agglomerated, manganese-silicate type flux for welding general structural steels and pipe steels. Provides sound welds in steels containing low silicon and manganese. Especially suitable for fillet and groove welds in steel contructions, LPG cylinder, pressure vessel production, spirally welding of pipes. Suitable to use at high welding speeds with single and multi-wires. Possible to use both in alternative and direct currents. Good wetting properties blending into the base metal, very easy slag removal in fillet and V-grooves. Provides flat and nice weld profile without undercut.
Standards and classifications
| EN ISO 14174 | S A MS/CS 1 |
| TS EN ISO 14174 | S A MS/CS 1 |
Typical chemical values of weld metal
| Welding Wire | Type of Analysis | C | Si | Mn | Mo |
|---|---|---|---|---|---|
| SW 701 | Weld Deposit | 0.04 | 0.45 | 1.45 | |
| SW 702 | Weld Deposit | 0.04 | 0.40 | 1.55 | |
| SW 702Mo | Weld Deposit | 0.04 | 0,50 | 1.65 | 0.45 |
| SW 702Si | Weld Deposit | 0.04 | 0.65 | 1.60 |
Typical mechanical values of weld metal
| Test Condition | Welding Wire | Yield Strength (N/mm²) | Tensile Strength (N/mm²) | Elongation A5 (%) | Charpy V-Notch Properties (J) | |
|---|---|---|---|---|---|---|
| As welded | SW 701 | 400 | 500 | 30 | 0°C → 70 | -20°C → 60 |
| As welded | SW 702 | 425 | 540 | 30 | 0°C → 65 | -20°C → 55 |
| As welded | SW 702Mo | 515 | 590 | 28 | 0°C → 60 | -20°C → 50 |
| As welded | SW 702Si | 450 | 550 | 30 | 0°C → 60 | -20°C → 50 |
Wire-flux combinations, standards
| Welding Wire | EN Designation of Wire | EN ISO/TS EN ISO 14171 - A | AWS Designation of Wire | AWS/ASME SFA 5.17/SFA 5.23 |
|---|---|---|---|---|
| SW 701 | S1 | S 38 2 MS/CS S1 | EL12 | F7A2-EL12 |
| SW 702 | S2 | S 42 2 MS/CS S2 | EM12 | F7A2-EM12 |
| SW 702Mo | S2Mo | S 46 2 MS/CS S2Mo | EA2 | F8A2-EA2 |
| SW 702Si | S2Si | S 42 3 MS/CS S2Si | EM12K | F7A2-EM12K |
Welding positions
Polarity
Variants and packaging
| Product Code | Weight Of The Box (kg) | Boxes Per Package | Weight Of The Package | Packaging Type |
|---|---|---|---|---|
| 401060AGM2 | 25.0 | 1 | 25.6 | Kraft Bag |
| 401060AHM2 | 25.0 | 1 | 25.6 | Kraft Bag |
Storage and re-drying
- The total drying duration should not exceed 10 hours (also for repeated drying).
- During transportation and storage, it should be ensured that the packaging is not damaged or torn.
- It has to be dried at 350°C for 2 hours.