Classification: S A CS 3 (EN ISO 14174)
Alloyed and agglomerated flux, which is designed for submerged arc hardfacing of parts subjected to metal to metal friction wear, moderate impart and low stress mineral abrasion.
Price and availability are provided by quotation. Send an enquiry with quantity and variant.
Product description
Alloyed and agglomerated flux, which is designed for submerged arc hardfacing of parts subjected to metal to metal friction wear, moderate impart and low stress mineral abrasion. Provides weld metal with 225-300 HB hardness, when used with SW 702 wire electrode. Possible to use in direct current. Hardness and transfer of alloying elements to the weld metal depens on welding parameters used. For instance, optimum welding parameters for 4.00 mm wire electrode are about 600 A, 32 V, 50 cm/min. welding speed. Gives very smooth and clean weld bead surfaces, slag removal is very easy and generally slag is self releasing. Typical Applications: Suitable for hardfacing of machine gear parts, rails, supports rolls of caterpillars, pulleys, locomotive wheels, table and support rolls in iron and steel industry.
Standards and classifications
| EN ISO 14174 | S A CS 3 |
| TS EN ISO 14174 | S A CS 3 |
Typical chemical values of weld metal
| Welding Wire | Type of Analysis | C | Si | Mn | Cr | Mo |
|---|---|---|---|---|---|---|
| SW 702 | Weld Deposit | 0.15 | 0.60 | 1.50 | 1.00 | 0.25 |
Typical mechanical values of weld metal
| Test Condition | Welding Wire | Hardness (HB) | Hardness (HRc) |
|---|---|---|---|
| As welded | SW 702 | 225-300 | 20 - 32 |
Welding positions
Polarity
Wear resistance
| Property | Level |
|---|---|
| Abrasion | Low |
| Adhesion | Medium |
| Impact | High |
| Temperature | Low |
| Corrosion | Low |
Scale as published in the official Magmaweld chart: Low · Medium · High · Very High
Variants and packaging
| Product Code | Weight Of The Box (kg) | Boxes Per Package | Weight Of The Package | Packaging Type |
|---|---|---|---|---|
| 408010AGM2 | 25.0 | 1 | 25.6 | Kraft Bag |
Storage and re-drying
- The total drying duration should not exceed 10 hours (also for repeated drying).
- During transportation and storage, it should be ensured that the packaging is not damaged or torn.
- It has to be dried at 350°C for 2 hours.